2D transition metal carbides and nitrides (MXenes) are actively pursued as pseudocapacitive materials for supercapacitors owing to their advantages in electronic conductivity and surface reactivity. Increasing the fraction of ─O terminal groups in Ti3 C2 Tx is a promising approach to improve the pseudocapacitive charge storage in H2 SO4 electrolytes, but it suffers from a lack of effective functionalization methods and stability of the groups in practical operation. Here a low-temperature and environment-friendly approach via the interaction of nonequilibrium plasmas with Ti3 C2 Tx dispersion is demonstrated to generate abundant and stable surface-terminating O groups. The impact of the discharge environment (Ar, O2 , and H2 ) on the structural characteristics and electrochemical performance of Ti3 C2 Tx nanosheets is studied. The Ti3 C2 Tx modified in Ar and H2 maintains their original morphology but a significantly lower F content. Consequently, an extraordinarily high content (78.5%) of surface-terminating O groups is revealed by the high-resolution X-ray photoelectron spectroscopy spectra for the Ti3 C2 Tx samples modified in H2 plasma-treated solutions. Additionally, the Ti3 C2 Tx treated using H2 plasmas exhibits the best capacitive performance of 418.3 F g-1 at 2 mV s-1 , which can maintain 95.88% capacity after 10 000 cycles. These results contribute to the development of advanced nanostructured pseudocapacitive electrode materials for renewable energy storage applications.
Keywords: MXene; energy storage; functional groups; nonthermal plasma; pseudocapacitive response.
© 2023 Wiley-VCH GmbH.