We reported exciton binding-energy determination using tunneling-current spectroscopy of Germanium (Ge) quantum dot (QD) single-hole transistors (SHTs) operating in the few-hole regime, under 405-1550 nm wavelength (λ) illumination. When the photon energy is smaller than the bandgap energy (1.46 eV) of a 20 nm Ge QD (for instance, λ = 1310 nm and 1550 nm illuminations), there is no change in the peak voltages of tunneling current spectroscopy even when the irradiation power density reaches as high as 10 µW/µm2. In contrast, a considerable shift in the first hole-tunneling current peak towards positive VG is induced (ΔVG ≈ 0.08 V at 0.33 nW/µm2 and 0.15 V at 1.4 nW/µm2) and even additional photocurrent peaks are created at higher positive VG values (ΔVG ≈ 0.2 V at 10 nW/µm2 irradiation) by illumination at λ = 850 nm (where the photon energy matches the bandgap energy of the 20 nm Ge QD). These experimental observations were further strengthened when Ge-QD SHTs were illuminated by λ = 405 nm lasers at much lower optical-power conditions. The newly-photogenerated current peaks are attributed to the contribution of exciton, biexciton, and positive trion complexes. Furthermore, the exciton binding energy can be determined by analyzing the tunneling current spectra.
© 2023. Springer Nature Limited.