Oxygen vacancies induced band gap narrowing for efficient visible-light response in carbon-doped TiO2

Sujun Guan; Yanling Cheng; Liang Hao; Hiroyuki Yoshida; Chiaki Tarashima; Tianzhuo Zhan; Takaomi Itoi; Tangbin Qiu; Yun Lu

doi:10.1038/s41598-023-39523-6

Oxygen vacancies induced band gap narrowing for efficient visible-light response in carbon-doped TiO₂

Sci Rep. 2023 Aug 29;13(1):14105. doi: 10.1038/s41598-023-39523-6.

Authors

Sujun Guan¹, Yanling Cheng², Liang Hao³, Hiroyuki Yoshida⁴, Chiaki Tarashima¹, Tianzhuo Zhan⁵, Takaomi Itoi⁶, Tangbin Qiu⁶, Yun Lu⁷

Affiliations

¹ Research Center for Space System Innovation, Tokyo University of Science, Chiba, Japan.
² Beijing Key Laboratory of Biomass Waste Resource Utilization, Beijing Union University, Beijing, China. cheng1012cn@aliyun.com.
³ College of Mechanical Engineering, Tianjin University of Science and Technology, Tianjin, China.
⁴ Chiba Industrial Technology Research Institute, Chiba, Japan.
⁵ Bio-Nano Electronics Research Centre, Toyo University, Saitama, Japan.
⁶ Graduate School and Faculty of Engineering, Chiba University, Chiba, Japan.
⁷ Graduate School and Faculty of Engineering, Chiba University, Chiba, Japan. luyun@faculty.chiba-u.jp.

Abstract

The band gap of rutile TiO₂ has been narrowed, via the formation of oxygen vacancies (OVs) during heat treatment in carbon powder (cHT) with embedding TiO₂ coatings. The narrowed band gap efficiently improves the visible light response of TiO₂ coatings, to further enhance the visible-light-driven photocatalytic activity. The change in OVs during cHT has been studied by manipulation of cHT temperature and time. The effect of OVs on the band structure of nonstoichiometric TiO_2-x has been further calculated by first-principles calculations. With raising the temperature, SEM images show that the nano-size fiber-like structure forms on the surface of TiO₂ coatings, and the amount of the fiber-like structure significantly increases and their size changes from nano to micro under 800 °C, contributing to cause an increase in accessible surface area. The UV-Vis results reveal that the band gap of TiO₂ has been narrowed during cHT, due to the formed oxygen vacancies. The XPS results further confirm that the formation of surface defects including OVs, and the XPS depth profile further shows the decreased relative amount of O whereas increased relative amount of carbon. Notably, after cHT for TiO₂ coatings, the photocatalytic activity first increases then decreases with raising the temperature, achieving approximately 3 times at 850 °C. The first-principles calculation suggest that the OVs in TiO₂ coatings with localized electrons could facilitate the band gap narrowing, further favoring to enhance the photocatalytic activity under visible light.