Biodegradable composite films based on mucilage from Opuntia ficus-indica (Cactaceae): Microstructural, functional and thermal properties

Abstract

This study evaluated the feasibility of using cactus mucilage (CM) to elaborate biobased composite films blended with styrene-butadiene rubber latex (SBL). The CM was extracted and precipitated with ethanol (CMET) and isopropanol (CMIS). Mucilage-based films were formulated using three levels of mucilage (4, 6, and 8 wt%). The microstructure, thickness, moisture content, density, water contact angle, water vapor permeability, film solubility, thermal stability, and toughness of mucilage films blended with SBL (SBL/CMET and SBL/CMIS) were measured. The properties of mucilage-based films varied systematically, depending on the concentration of mucilage. The addition of SBL to CM film produces compatible, hydrophobic, flexible, and stiffer films with low moisture contents and good barrier properties. The mucilage film incorporated with 6 wt% CMET and CMIS reached the highest Young's modulus of 1512 ± 21 and 1988 ± 55 MPa, respectively. The DSC of produced films reveals that the Tg of SBL/CMIS is lower than that of SBL/CMIS. The synthesized films were structurally stable at high temperatures. The biodegradability of the composite films buried in the ground shows that the produced films are 100 % biodegradable after 40 days. Thus, CM blended with SBL can benefit specific applications, especially food packaging.

Keywords: Biodegradable; Film; Opuntia ficus-indica; SBL; Thermal stability; cactus mucilage.