The constant change in microplastics (MP) due to exposure to environmental conditions leads to physical and chemical changes that enhance their ability to transport other pollutants, increasing the concern about their widespread presence in the environment. This work aimed to simulate the aging process of six MP (polyamide 6, unplasticized polyvinyl chloride, low-density polyethylene, polystyrene, polyethylene-co-vinyl acetate, polypropylene) in freshwater and seawater ecosystems at laboratory scale and evaluate its effects through optical microscope observation, Fourier transform infrared spectroscopy-Attenuated Total Reflectance (FTIR-ATR), Raman spectroscopy, and thermal gravimetric analysis (TGA). Through a combined experimental study of aged MP, the degradation by UV interaction was evidenced by the appearance of new infrared bands in the FTIR spectra assigned to ketones and hydroxyl groups. While Raman analysis and microscope images reveal the appearance of pores, wrinkles, and roughness in the MP surfaces. Variations in the temperature of the maximum weight loss of the MP were observed in the TGA analysis. The adsorption of chlorpyrifos (CPF), a common pesticide widely used in agriculture, by the pristine and aged MP was also studied. The highest affinity for CPF was observed for pristine LDPE and the lowest for PP. The batch adsorption studies revealed an increase in adsorption capacity as a consequence of the aging process for both MP. These results proved that the weathering effects caused changes in the behavior of MP, namely in the interaction with other pollutants.
Keywords: aged microplastic; pristine microplastic; river water ecosystems; seawater ecosystems; weathering effects.