In this study, we fabricated a cellulose nanocrystal (CNC)-embedded aerogel-like chitosan foam and carbonized the 3D foam for electrical energy harvesting. The nanocrystal-supported cellulose foam can demonstrate a high surface area and porosity, homogeneous size ranging from various microscales, and a high quality of absorbing external additives. In order to prepare CNC, microcrystalline cellulose (MCC) was chemically treated with sulfuric acid. The CNC incorporates into chitosan, enhancing mechanical properties, crystallization, and generation of the aerogel-like porous structure. The weight percentage of the CNC was 2 wt% in the chitosan composite. The CNC/chitosan foam is produced using the freeze-drying method, and the CNC-embedded CNC/chitosan foam has been carbonized. We found that the degree of crystallization of carbon structure increased, including the CNCs. Both CNC and chitosan are degradable materials when CNC includes chitosan, which can form a high surface area with some typical surface-related morphology. The electrical cyclic voltammetric result shows that the vertical composite specimen had superior electrochemical properties compared to the horizontal composite specimen. In addition, the BET measurement indicated that the CNC/chitosan foam possessed a high porosity, especially mesopores with layer structures. At the same time, the carbonized CNC led to a significant increase in the portion of micropore.
Keywords: carbonized structure; cellulose nanocrystal; chitosan; voltammetric.