The use of alternative raw materials, such as agricultural biomass and by-products, in particleboard (PB) production is a viable approach to address the growing global demand for sustainable wood-based materials. The purpose of this study was to investigate the effect of the type of hardener and tannin-glyoxal (TG) adhesive formulation on the cohesion and adhesion performance of TG adhesives for areca-based PB. Two types of hardeners were used, NH4Cl and NaOH, and three adhesive formulations with tannin:glyoxal ratios (i.e., F1 (1:2), F2 (1:1), and F3 (2:1)) were applied to improve the cohesion performance and adhesion for areca-based TG adhesive for PB. The basic, chemical, and mechanical properties of the TG adhesive were investigated using a Fourier transform infrared spectrometer, rotational rheometer, dynamic mechanical analyzer (DMA), and X-ray diffractometer. The results show that a high glyoxal percentage increases the percentage of crystallinity in the adhesive. This shows that the increase in glyoxal is able to form better polymer bonds. DMA analysis shows that the adhesive is elastic and the use of NH4Cl hardener has better mechanical properties in thermodynamic changes than the adhesive using NaOH hardener. Finally, the adhesion performance of the TG adhesives on various types of hardeners and adhesive formulations was evaluated on areca-based PB panels. Regardless of the type of hardener, the TG adhesive made with F1 had better cohesion and adhesion properties compared to F2 and F3. Combining F1 with NH4Cl produced areca-based PB panels with better physical and mechanical qualities than the adhesive formulations F2 and F3, and complied with Type 8 particleboard according to SNI 03-2105-2006 standard.
Keywords: adhesive strength; areca particleboard; bio-based adhesives; cohesive strength; glyoxalated tannin.