This study evaluated the bonding characteristics of a silane coupling agent (SCA) and a methyl methacrylate (MMA)-containing primer (MCP) for 11 types of commercial composite blocks (CBs) for sandblasted and non-sandblasted surfaces. The shear bond strength (SBS) was measured according to ISO 29022: Notched-edge shear bond strength test. The SBS results demonstrated statistically significant differences between the CBs under all identical conditions. For the non-sandblasted groups, the SBSs of MCP-treated specimens were significantly higher than those of SCA-treated specimens for all but two CBs. Comparing the two treatments in sandblasted groups, the SBS was significantly higher for seven out of 11 MCP-treated RCB specimens, in contrast with three cases for the SCA-treated group. Two-way ANOVA for SBS showed the interaction effect between sandblasting and primer type for specific CBs, indicating that the sandblasting treatment improved SBS more effectively for SCA-treated specimens. Moreover, the effect of the SCA treatment was more material-dependent compared to that of the MCP treatment, which did not achieve a strong bond in all CBs but proved more effective than the SCA treatment, especially for non-sandblasted surfaces.
Keywords: CAD/CAM; bond strength; composites; resin primer; sandblast; silane coupling agent.