Currently, catalytic pyrolysis has become a versatile and highly useful technology in the treatment of different plastic wastes. Thus, the development of selective catalysts to carry out cracking reactions and obtain a greater fraction of the desired products is essential. This study focuses on the synthesis of monometallic (Ni) and bimetallic (Ni-Zn) catalysts supported on ZSM-5 zeolite using an impregnation and co-impregnation method, respectively. The obtained catalysts were characterized by FTIR spectroscopy, N2 adsorption/desorption measurements, scanning electron microscopy (SEM) and energy dispersive X-Ray spectroscopy (EDS), temperature programmed NH3 desorption (TPD-NH3) and thermogravimetric analysis (TGA). In this way, a mixture of polystyrene and polypropylene recycled with a catalyst/plastic waste ratio of 1:500 was used for pyrolysis tests. The best results were obtained using the Ni-Zn/ZSM-5 catalyst, which included better impregnation, increased surface acidity, decreased dispersion and a shorter reaction time in the catalytic pyrolysis process. Under the optimized conditions, catalytic pyrolysis showed an excellent performance to generate hydrocarbons of greater industrial interest.
Keywords: ZSM-5; bimetallic; catalyst; catalyst acidity; catalyst properties; monometallic.