Li2 MnO3 has been contemplated as a high-capacity cathode candidate for Li-ion batteries; however, it evolves oxygen during battery charging under ambient conditions, which hinders a reversible reaction. However, it is unclear if this irreversible process still holds under subambient conditions. Here, the low-temperature electrochemical properties of Li2 MnO3 in an aqueous LiCl electrolyte are evaluated and a reversible discharge capacity of 302 mAh g-1 at a potential of 1.0 V versus Ag/AgCl at -78 °C with good rate capability and stable cycling performance, in sharp contrast to the findings in a typical Li2 MnO3 cell cycled at room temperature, is observed. However, the results reveal that the capacity does not originate from the reversible oxygen oxidation in Li2 MnO3 but the reversible Cl2 (l)/Cl- (aq.) redox from the electrolyte. The results demonstrate the good catalytic properties of Li2 MnO3 to promote the Cl2 /Cl- redox at low temperatures.
Keywords: Li2MnO3; aqueous batteries; catalysis; chlorine; low temperatures.