Plant-derived thermoplastic polyester elastomer (TPEE) is an environment friendly polymer known for its exceptional tear strength and mechanical properties, whose monomers are generated from crops. To prepare high-performance TPEE foams is still challenging due to the intrinsic shrinkage behavior. Herein, two microcellular foaming routes with different charging orders of mixed blowing agents, namely "CO2 firstly charging process (CO2-F-process)" and "N2 firstly charging process (N2-F-process)", were developed to elucidate the effects of mixed blowing agents on foaming behavior. Compared with the case in N2-F-process, more carbon dioxide and less nitrogen were adsorbed in CO2-F-process. Thus, TPEE foams prepared by N2-F-process show less shrinkage and higher creep recovery ratio than those prepared by CO2-F-process. Thanks to better structural stability and smaller shrinkage, TPEE foams prepared by N2-F-process exhibited enhanced strength and resilience. For the foams with similar density, compression strength can be increased by 52 %, and energy loss coefficient can be reduced to 50 %, by using N2-F-process. Thus, not only biomass TPEE foams with enhanced mechanical performance shows promising prospects in those areas that needs lightweight, insulation and high resilience, but also novel microcellular foaming technique with mixed blowing agents opens a new way for developing high-performance polymeric foams.
Keywords: Biomass TPEE; Microcellular foaming; Mixed blowing agents.
Copyright © 2023 Elsevier B.V. All rights reserved.