Severe capacity/voltage fading still poses substantial obstacles in the commercial applications of Li-rich layered oxides, which stems from the aggregation of Li2MnO3-like domains and unstable surface structure. Here, we report highly stabilized Co-free Li1.2Ni0.2Mn0.6O2 with uniformly dispersed Li2MnO3-like domains and a protective rock-salt structure shell by reducing the oxygen partial pressure during high-temperature calcination. Experimental characterizations and DFT calculations reveal that the uniformly dispersed and small-sized Li2MnO3-like domains suppress the peroxidation of lattice oxygen, enabling highly reversible oxygen redox and excellent structural stability. Moreover, the induced rock-salt structure shell significantly restrains lattice oxygen release, TM dissolution, and interfacial side reactions, thereby improving the interfacial stability and facilitating Li+ diffusion. Consequently, the obtained Li1.2Ni0.2Mn0.6O2 which was calcinated under an oxygen partial pressure of 0.1% (LNMO-0.1) delivers a high reversible capacity of 276.5 mAh g-1 at 0.1 C with superior cycling performance (a capacity retention rate of 85.4% after 300 cycles with a small voltage fading rate of 0.76 mV cycle-1) and excellent thermal stability. This work links the synthesis conditions with the domain structure and electrochemical performance of Li-rich cathode materials, providing some insights for designing high-performance Li-rich cathodes.
Keywords: Co-free Li-rich layered oxides; Li2MnO3-like domains; cycling stability; disordered rock-salt structure shell; oxygen partial pressure.