The lack of well-developed repair techniques limits the use of thermoplastic composites in commercial aircraft, although trends show increased adoption of composite materials. In this study, high-performance thermoplastic composites, viz., carbon fibre (CF) reinforced Polyetherketoneketone (PEKK) and Polyether ether ketone (PEEK), were subjected to low-velocity impact tests at 20 J. Post-impact, the damaged panels were repaired using an induction welder by applying two different methods: induction welding of a circular patch to the impacted area of the laminate (RT-1); and induction welding of the impacted laminates under the application of heat and pressure (RT-2). The panels were subjected to compression-after-impact and repair (CAI-R), and the results are compared with those from the compression-after-impact (CAI) tests. For CF/PEKK, the RT-1 and RT-2 resulted in a 13% and 7% higher strength, respectively, than the value for CAI. For CF/PEEK, the corresponding values for RT-1 and RT-2 were higher by 13% and 17%, respectively. Further analysis of the damage and repair techniques using ultrasonic C-scans and CAI-R tests indicated that induction welding can be used as a repair technique for industrial applications. The findings of this study are promising for use in aerospace and automotive applications.
Keywords: CF/PEEK; CF/PEKK; carbon fibre reinforced thermoplastics; compression after impact; fusion bonding; induction welding; repair.