Plant fiber-reinforced polylactic acid (PLA) exhibits excellent mechanical properties and environmental friendliness and, therefore, has a wide range of applications. This study investigated the mechanical properties of three short plant fiber-reinforced PLA composites (flax, jute, and ramie) using mechanical testing and material characterization techniques (SEM, FTIR, and DSC). Additionally, we propose a methodology for predicting the mechanical properties of high-content short plant fiber-reinforced composite materials. Results indicate that flax fibers provide the optimal reinforcement effect due to differences in fiber composition and microstructure. Surface pretreatment of the fibers using alkali and silane coupling agents increases the fiber-matrix interface contact area, improves interface performance, and effectively enhances the mechanical properties of the composite. The mechanical properties of the composites increase with increasing fiber content, reaching the highest value at 40%, which is 38.79% higher than pure PLA. However, further increases in content lead to fiber agglomeration and decreased composite properties. When the content is relatively low (10%), the mechanical properties are degraded because of internal defects in the material, which is 40.42% lower than pure PLA. Through Micro-CT technology, the fiber was reconstructed, and it was found that the fiber was distributed mainly along the direction of injection molding, and the twin-screw process changes the shape and length of the fiber. By introducing the fiber agglomeration factor function and correcting the Halpin-Tsai criterion, the mechanical properties of composite materials with different contents were successfully predicted. Considering the complex stress state of composite materials in actual service processes, a numerical simulation method was established based on transversely isotropic material using the finite element method combined with theoretical analysis. The mechanical properties of high-content short plant fiber-reinforced composite materials were successfully predicted, and the simulation results showed strong agreement with the experimental results.
Keywords: PLA; mechanical properties; performance prediction; short plant fiber; surface treatments.