The interest in low processing temperature for printable transistors is rapidly increasing with the introduction of a new form factor in electronics and the growing importance of high throughput. This paper reports the fabrication of low-temperature-processable enhancement-mode amorphous oxide thin-film transistors (TFTs) using the solution process. A facile low-pressure annealing (LPA) method is proposed for the activation of indium oxide (InOx) semiconductors at a significantly low processing temperature of 200 °C. Thermal annealing at a pressure of about ~10 Torr induces effective condensation in InOx even at a low temperature. As a result, the fabricated LPA InOx TFTs not only functioned in enhancement mode but also exhibited outstanding switching characteristics with a high on/off current ratio of 4.91 × 109. Furthermore, the LPA InOx TFTs exhibit stable operation under bias stress compared to the control device due to the low concentration of hydroxyl defects.
Keywords: enhancement mode; low processing temperature; low-pressure annealing; metal-oxide semiconductor; solution process; thin-film transistors.