Nickel ferrite nanoparticles are prepared by using a low-temperature self-propagating solution combustion method using urea as fuel. The prepared nickel ferrite nanoparticles were doped with polyaniline in the three different weight ratios of 10%, 30% and 50% by using an in situ polymerization method and by adding ammonium persulfate as an oxidizing agent. The obtained samples were characterized by using XRD, FTIR, SEM and a UV-visible spectrophotometer. XRD examined crystalline peaks of ferrites and amorphous peak of polyaniline and confirmed the formation of the composites. FTIR examined the chemical nature of samples and showed peaks due to polyaniline and the characteristic peaks that were less than 1000 cm-1 wavenumber were due to metal-oxygen bond vibrations of ferrites. AC conductivity increased with frequency in all samples and the highest AC conductivity was seen in polyaniline/nickel ferrite 50%. DC conductivity increased in all samples with the temperature showing the semiconducting nature of the samples. Activation energy was evaluated by using Arrhenius plots and there was a decrease in activation energy with the addition of ferrite content. The UV-visible absorption peaks of polyaniline showed shifting in the composites. The optical direct and indirect band gaps were evaluated by plotting Tauc plots and the values of the optical band gap decreased with addition of ferrite in polyaniline and the Urbach energy increased in the samples with 10%, 30% and 50% polyaniline/nickel ferrite composites. The optical properties of these composites with a low band gap can find applications in devices such as solar cells.
Keywords: electrical conductivity; nanoferrite; optical property; solution combustion.