The formation of a cellular hierarchically organized NiO film on a carbon paper substrate under hydrothermal conditions using triethanolamine as a base has been studied. The thermal behavior of the carbon paper substrate with the applied semi-product shell was studied using synchronous thermal analysis (TGA/DSC) and it was demonstrated that such modification of the material surface leads to a noticeable increase in its thermal stability. Using scanning electron microscopy (SEM), it was shown that the NiO film grown on the carbon fiber surface is characterized by a complex cellular morphology, organized by partially layered individual nanosheets of about 4-5 nm thickness and lateral dimensions up to 1-2 μm, some edges and folds of which are located vertically relative to the carbon fiber surface. The surface of the obtained material was also examined using atomic force microscopy (AFM), and the electronic work function of the oxide shell surface was evaluated using the Kelvin probe force microscopy (KPFM) method. The electrochemical parameters of the obtained flexible NiO/CP electrode were analyzed: the dependence of the specific capacitance on the current density was determined and the stability of the material during cycling was studied, which showed that the proposed approach is promising for manufacturing hierarchically organized electrodes for flexible supercapacitors.
Keywords: NiO; flexible electrode; hierarchical microstructure; hydrothermal synthesis; nanosheets; supercapacitor; thin films.