In situ preparation of double gradient anode materials based on polysiloxane for lithium-ion batteries

Siqi Guan; Chen Xu; Yuanjiang Chen; Yongjin Zhang; Lixiang Li; Han Zhang; Baigang An; Haiming Yang; Weimin Zhou; Chengguo Sun; Dongying Ju; Xin Geng

doi:10.1039/d3na00285c

In situ preparation of double gradient anode materials based on polysiloxane for lithium-ion batteries

Nanoscale Adv. 2023 Jun 22;5(16):4158-4166. doi: 10.1039/d3na00285c. eCollection 2023 Aug 8.

Authors

Siqi Guan¹, Chen Xu¹, Yuanjiang Chen¹, Yongjin Zhang¹, Lixiang Li^{1

2}, Han Zhang¹, Baigang An^{1

2}, Haiming Yang^{1

2}, Weimin Zhou^{1

2}, Chengguo Sun^{1

3}, Dongying Ju², Xin Geng^{1

2}

Affiliations

¹ Institute of Energy Materials and Electrochemistry Research, University of Science and Technology Liaoning Anshan 114051 PR China gengxin60@163.com bgan@ustl.edu.cn.
² Hainan Provincial Key Lab of Fine Chemistry, School of Chemical Engineering and Technology, Hainan University Haikou 570228 China.
³ School of Chemical Engineering, Nanjing University of Science and Technology Nanjing 210094 China.

Abstract

Although silicon has a high volumetric energy density as an anode material for Li-ion batteries, its volumetric expansion and sluggish Li⁺ migration kinetics need to be urgently addressed. In this work, cage-like structure materials (HRPOSS) derived from the in situ hydrogen reduction of polyhedral oligomeric silsesquioxane (T8-type POSS) were constructed as an Si@C anode for Li-ion batteries. Benefiting from the intriguing features of the Si/N double gradient and even-distributed silicon, HRPOSS-6 exhibited faint volume changes and fast ion-electron kinetics. Moreover, the uniformly immobilized nano-silicic and concentration gradient were favorable for accelerated ion migration. Therefore, HRPOSS-6 exhibited good electrochemical performances given that its cage structure could relieve the volume expansion. HRPOSS-6 demonstrated a high reversible capacity of 1814.1 mA h g^-1 and long cycling performance after 200 cycles with 635 mA h g^-1 at a current density of 0.5 A g^-1. Accordingly, this Si/C/N composite exhibited great potential for high energy Li-ion batteries, where the corresponding full-cell (HRPOSS-6//LiNi_0.6Co_0.2Mn_0.2O₂) showed a cycle life of 200 cycles with over 80% capacity retention at rate of 1C. This work exploits the concentration gradients of dual elements for the capacity improvement of Si anodes and offers insight into the development of high-performance Si@C anode materials for advanced Li-ion batteries.