Developing non-carbon-based adsorbents is essential for removing heavy metals from post-incineration flue gas. In this study, a new high-temperature-resistant adsorbent-activated boron nitride (BN) was prepared using precursors combined with a high-temperature activation method. The adsorption characteristics of BN for Zn, Cu, and Cd in simulated flue gas and sludge incineration flue gas were investigated using gas-phase heavy metal adsorption experiments. The results showed that BN prepared at 1350 °C for 4 h had defect structures, abundant pores, functional groups, and a high specific surface area of 658 m2/g. The adsorption capacity of BN in simulated flue gases decreases with increasing adsorption temperature, whereas it is always higher than that of activated carbon (AC). The total adsorption capacities for Zn, Cu, and Cd were the highest at 50 °C with 48.3 mg/g. BN had strong adsorption selectivity for Zn, with a maximum adsorption capacity of 54.45 mg/g, and its adsorption process occurred mainly on the surface. Cu and Cd inhibited Zn adsorption, leading to a decrease in the Zn adsorption capacity. In sludge incineration flue gas, BN can quickly reach adsorption equilibrium. The BN had a synergistic disposal capacity for heavy metals and fine particulate matter. The maximum adsorption capacity was reduced compared to the simulated flue gas adsorption capacity, which was 5.1 mg/g. However, BN still exhibited a strong adsorption selectivity for Zn, and its adsorption capacity was always greater than that of AC. The rich functional groups and high specific surface area enable BN to physically and chemically double-adsorb heavy metals.
© 2023 The Authors. Published by American Chemical Society.