Currently, energy efficiency and saving in production engineering, including Material Extrusion (MEX) Additive Manufacturing, are of key importance to ensure process sustainability and cost-effectiveness. The functionality of parts made with MEX 3D-printing remains solid, especially for expensive high-performance polymers, for biomedical, automotive, and aerospace industries. Herein, the energy and tensile strength metrics are investigated over three key process control parameters (Nozzle Temperature, Layer Thickness, and Printing Speed), with the aid of laboratory-scale PEEK filaments fabricated with melt extrusion. A double optimization is attempted for the production by consuming minimum energy, of PEEK parts with improved strength. A three-level Box-Behnken design with five replicas for each experimental run was employed. Statistical analysis of the experimental findings proved that LT is the most decisive control setting for mechanical strength. An LT of 0.1 mm maximized the tensile endurance (∼74 MPa), but at the same time, it was responsible for the worst energy (∼0.58 MJ) and printing time (∼900 s) expenditure. The experimental and statistical findings are further discussed and interpreted using fractographic SEM and optical microscopy, revealing the 3D printing quality and the fracture mechanisms in the samples. Thermogravimetric analysis (TGA) was performed. The findings hold measurable engineering and industrial merit, since they may be utilized to achieve an optimum case-dependent compromise between the usually contradictory goals of productivity, energy performance, and mechanical functionality.
Keywords: 3D printing; Box-Behnken; Energy consumption; Fused filament fabrication (FFF); Material extrusion; Mechanical response; Polyetheretherketone (PEEK).
© 2023 The Authors.