Fabrication and optical properties of garnet ceramics based on Y3- xScxAl5O12 doped with ytterbium and erbium

V A Tarala; S V Kuznetsov; O M Chapura; F F Malyavin; E A Brazhko; A A Kravtsov

doi:10.1039/d3dt01453c

Fabrication and optical properties of garnet ceramics based on Y_{3- x}Sc_xAl₅O₁₂ doped with ytterbium and erbium

Dalton Trans. 2023 Aug 15;52(32):11285-11296. doi: 10.1039/d3dt01453c.

Authors

V A Tarala¹, S V Kuznetsov², O M Chapura¹, F F Malyavin¹, E A Brazhko¹, A A Kravtsov¹

Affiliations

¹ North Caucasian Federal University, 1 Pushkin Str., Stavropol, 355017, Russian Federation.
² Prokhorov General Physics Institute of the Russian Academy of Sciences, 38 Vavilov str., Moscow, 119991, Russian Federation. kouznetzovsv@gmail.com.

PMID: 37528695
DOI: 10.1039/d3dt01453c

Abstract

Optical ceramics YSAG:Yb,Er with an average grain size of 6 ± 1 microns were fabricated by vacuum sintering of nanocrystalline powders of the compositions Y_2.34Yb_0.45Er_0.09Sc_0.20Al_4.92O₁₂, Y_1.66Yb_0.45Er_0.09Sc_1.00Al_4.80O₁₂ and Y_0.96Yb_0.45Er_0.09Sc_1.70Al_4.80O₁₂. The linear transmittance coefficients of the YSAG:Yb,Er ceramic samples exceed 80% in the visible and infrared regions. The refractive index of ceramics increased from 1.827 to 1.859 with an increase in scandium content. The effect of scandium cations at the dodecahedral site of the YSAG crystal lattice on the optical and luminescence characteristics of Yb³⁺ (²F_7/2 and ²F_5/2) and Er³⁺ (⁴I_15/2, ⁴I_13/2, ⁴F_9/2 and ⁴S_13/2) in wavelength ranges of 530-690 nm, 890-1080 nm, and 1430-1680 nm was revealed.