In this study, we conducted direct synthesis of a dual metal-organic framework (Ni/Co-Hemin MOF) on phosphorous-doped reduced graphene oxide (PrGO) to serve as an active material in high-performance asymmetrical supercapacitors. The nanocomposite was utilized as an active material in supercapacitors, exhibiting a noteworthy specific capacitance of 963 C g-1 at 1.0 A g-1, along with a high rate capability of 68.3% upon increasing the current density by 20 times, and superior cycling stability. Our comprehensive characterization and control experiments indicated that the improved performance can be attributed to the combined effect of the dual MOF and the presence of phosphorous, influencing the battery-type supercapacitor behavior of GO. Additionally, we fabricated an asymmetric hybrid supercapacitor (AHSC) using Ni/Co-Hemin/PrGO/Nickel foam (NF) and activated carbon (AC)/NF. This AHSC demonstrated a specific capacitance of 281 C g-1 at 1.0 A g-1, an operating voltage of 1.80 V, an impressive energy density of 70.3 Wh kg-1 at a high power density of 0.9 kW kg-1. Notably, three AHSC devices connected in series successfully powered a clock for approximately 42 min. These findings highlight the potential application of Hemin-based MOFs in advanced supercapacitor systems.
© 2023. The Author(s).