Developing stable silicon-based and lithium metal anodes still faces many challenges. Designing new highly practical silicon-based anodes with low-volume expansion and high electrical conductivity, and inhibiting lithium dendrite growth are avenues for developing silicon-based and lithium metal anodes, respectively. In this study, SiOx Cy microtubes are synthesized using a chemical vapor deposition method. As Li-ion battery anodes, the as-prepared SiOx Cy not only combines the advantages of nanomaterials and the practical properties of micromaterials, but also exhibits high initial Coulombic efficiency (80.3%), low volume fluctuations (20.4%), and high cyclability (98% capacity retention after 1000 cycles). Furthermore, SiOx Cy , as a lithium deposition substrate, can effectively promote the uniform deposition of metallic lithium. As a result, low nucleation overpotential (only 6.0 mV) and high Coulombic efficiency (≈98.9% after 650 cycles, 1.0 mA cm-2 and 1.0 mAh cm-2 ) are obtained on half cells, as well as small voltage hysteresis (only 9.5 mV, at 1.0 mA cm-2 ) on symmetric cells based on SiOx Cy . Full batteries based on both SiOx Cy and SiOx Cy @Li anodes demonstrate great practicality. This work provides a new perspective for the simultaneous development of practical SiOx Cy and dendrite-free lithium metal anodes.
Keywords: Li metal anodes; SiOxCy; lithium dendrites; lithium-ion batteries; microtubes.
© 2023 Wiley-VCH GmbH.