Silicon-based microchannel technology offers unmatched performance in the cooling of silicon pixel detectors in high-energy physics. Although Si-Si direct bonding, used for the fabrication of cooling plates, also meets the stringent requirements of this application (its high-pressure resistance of ~200 bar, in particular), its use is reported to be a challenging and expensive process. In this study, we evaluated two alternative bonding methods, aiming toward a more cost-effective fabrication process: Si-Glass-Si anodic bonding (AB) with a thin-film glass, and Au-Au thermocompression (TC). The bonding strengths of the two methods were evaluated with destructive pressure burst tests (0-690 bar) on test structures, each made of a 1 × 2 cm2 silicon die etched with a tank and an inlet channel and sealed with a plain silicon die using either the AB or TC bonding. The pressure resistance of the structures was measured to be higher for the TC-sealed samples (max. 690 bar) than for the AB samples (max. 530 bar), but less homogeneous. The failure analysis indicated that the AB structure resistance was limited by the adhesion force of the deposited layers. Nevertheless, both the TC and AB methods provided sufficient bond quality to hold the high pressure required for application in high-energy physics pixel detector cooling.
Keywords: anodic bonding; bonding technology; burst pressure test; microcooling; microfluidic device; thermocompression bonding.