The aim of this work is to study the structural, dielectric, and mechanical properties of aluminum oxide ceramics with the triple sintering additive 4CuO-TiO2-2Nb2O5. With an increase in sintering temperature from 1050 to 1500 °C, the average grain size and the microhardness value at a load of 100 N (HV0.1) increased with increasing density. It has been shown that at a sintering temperature of 1300 °C, the addition of a 4CuO-TiO2-2Nb2O5 additive increases the low-frequency permittivity (2-500 Hz) in alumina ceramic by more than an order of magnitude due to the presence of a quadruple perovskite phase. At the same time, the density of such ceramics reached 89% of the theoretical density of α-Al2O3, and the microhardness value HV0.1 was 1344. It was observed that the introduction of 5 wt.% 4CuO-TiO2-2Nb2O5 in the raw mixture remarkably increases values of shrinkage and density of sintered ceramics. Overall, the results of this work confirmed that introducing the 4CuO-TiO2-2Nb2O5 sintering additive in the standard solid-phase ceramics route can significantly reduce the processing temperature of alumina ceramics, even when micron-sized powders are used as a starting material. The obtained samples demonstrated the potential of α-Al2O3 with the triple additive in such applications as electronics, microwave technology, and nuclear power engineering.
Keywords: alumina ceramics; dielectric permittivity; hardening; perovskite phase; the effect of the triple additive.