Ion exchange membranes, especially cation exchange membranes (CEMs), are an important component in membrane-based energy generation and storage because of their ability to transport cations via the electrochemical potential gradient while preventing electron transport. However, developing a CEM with low areal resistance, high permselectivity, and stability remains difficult. In this study, electrospun graphene oxide/polyethersulfone (GO/PES) composite nanofibers were prepared with varying concentrations of GO. To fabricate a CEM, the pores of the electrospun GO/PES nanofiber substrates were filled with a Nafion ionomer. The pore-filled PES nanofiber loaded with 1% GO revealed a noticeable improvement in hydrophilicity, structural morphology, and mechanical properties. The 1% GO/PES pore-filled CEM was compared to a Nafion membrane of a varying thickness and without a nanofiber substrate. The CEM with a nanofiber substrate showed permselectivity of 85.75%, toughness of 111 J/m3, and areal resistance of 3.7 Ω cm2, which were 12.8%, 4.3 times, and 4.0 times better, respectively, than those of the Nafion membrane at the same thickness. The development of a reinforced concrete-like GO/PES nanofiber structure containing stretchable ionomer-enhanced membrane surfaces exhibited suitable areal resistance and reduced the thickness of the composite membrane without compromising the mechanical strength, suggesting its potential application as a cation exchange membrane in electrochemical membrane-based systems.
Keywords: areal resistance; electrospinning; graphene oxide; ion exchange membrane; nanofiber; permselectivity; polyethersulfone; pore-filled.