Electrochemical capacitors operating in an aqueous electrolyte solution have become ever-more popular in recent years, mainly because they are cheap and ecofriendly. Additionally, aqueous electrolytes have a higher ionic conductivity than organic electrolytes and ionic liquids. These materials can exist in the form of a liquid or a solid (hydrogel). The latter form is a very promising alternative to liquid electrolytes because it is solid, which prevents electrolyte leakage. In our work, hydrogel polymer electrolytes (HPEs) were obtained via photopolymerization of a mixture of acrylic oligomer Exothane 108 with methacrylic acid (MAA) in ethanol, which was later replaced by electrolytes (1 M Na2SO4). Through the conducted research, the effects of the monomers ratio and the organic solvent concentration (ethanol) on the mechanical properties (tensile test), electrolyte sorption, and ionic conductivity were examined. Finally, hydrogel polymer electrolytes with high ionic conductivity (σ = 26.5 mS∙cm-1) and sufficient mechanical stability (σmax = 0.25 MPa, εmax = 20%) were tested using an AC/AC electrochemical double layer capacitor (EDLC). The electrochemical properties of the devices were investigated via cyclic voltammetry, galvanostatic charge/discharge, and impedance spectroscopy. The obtained results show the application potential of the obtained HPE in EDLC.
Keywords: electrochemical capacitor; hydrogel polymer electrolyte; photopolymerization.