To assess the in vitro and in situ effect of experimental combined fluoride and calcium nanocomposite solutions on dental caries prevention. Nanocompound mesoporous silica (MS) with calcium (Ca) and sodium fluoride (NaF) - (MSCaNaF); MS with NaF (MSNaF), NaF solution (positive control), and deionized water (negative control - CG) were studied. The specimens (n=130) were submitted in vitro to a multispecies biofilm in the presence of 2% sucrose. After 24 h and 48 h, the culture medium pH, the percent of surface mineral loss (%SML), and lesion depth (ΔZ) were analyzed. In the in situ study, 10 volunteers participated in four phases of 7-days each. The products were applied on the specimens (n=240) before 20% sucrose solution drips. The polysaccharides (SEPS and IEPS), %SML and roughness (Sa) were evaluated. There was an in vitro decrease in pH values in 24h and 48h, compared to baseline. The MSCaNaF and MSNaF groups obtained lower values of %SML and ΔZ (p < 0.05) than CG and NaF after 24h and were similar to NaF after 48h (p<0.05). In situ results showed similar SEPS and IEPS among all groups after 48h. An after 7-days, the nanocomposites had similar values (p>0.05), while NaF was similar to CG (p>0.05). After 48h, the MSCaNaF and MSNaF reduced the %SML (p<0.05). After 7-days, both experimental nanocomposites were similar to NaF (p>0.05). Regarding Sa, MSCaNaF was better than NaF for both periods (p<0.05). The nanocomposites controlled the in vitro and in situ enamel demineralization, mainly in the initial periods.