In this study, an isotropic etching process of SiO2 selective to Si3N4 using NF3/H2/methanol chemistry was investigated. HF was formed using a NF3/H2 remote plasma, and in order to remove the F radicals, which induces spontaneous etching of Si-base material, methanol was injected outside the plasma discharge region. Through this process, etch products were formed on the surface of SiO2, and then the (NH4)2SiF6 was removed by following heating process. When the H and F radicals were abundant, the highest SiO2 etch per cycle (EPC) was obtained. And, the increase of H2 and methanol percentage in the gas chemistry increased the etch selectivity by decreasing the F radicals. The etch products such as (NH4)2SiF6 were formed on the surfaces of SiO2 and Si3N4 during the reaction step and no noticeable spontaneous etching by formation of SiF4 was observed. By optimized conditions, the etch selectivity of SiO2 over Si3N4 and poly Si higher than 50 and 20, respectively, was obtained while having SiO2 EPC of ~ 13 nm/cycle. It is believed that the cyclic process using NF3/H2 remote plasma and methanol followed by heating can be applied to the selective isotropic SiO2 etching of next generation 3D device fabrication.
© 2023. The Author(s).