Poly (methyl methacrylate) (PMMA), is an acrylic polymer substance that is mostly used for denture base applications. The purpose of this laboratory study was to investigate the effect of adding 0.05 wt.% Ag-doped carbon nanotubes (CNT) to PMMA-based (PMMA and MMA) denture base material on the impact strength, microhardness, and antimicrobial activity. A total of 60 heat-cured acrylic resin specimens were prepared. The specimens were randomly divided into two main groups (n = 30/group), according to the powder used: (a) control group, using heat-cured PMMA; (b) treatment group, using a powder prepared by blending 0.05 wt.% silver-doped CNT nanoparticles with heat-cured PMMA. The impact strength, microhardness and anticandidal activity for each group were assessed via the Charpy, Vickers and agar diffusion tests, respectively (n = 10/test for each subgroup). Data were analyzed using independent-sample t-tests (p ≤ 0.05). The results of the impact strength test revealed that the treated heat-cured PMMA-MMA with Ag-doped CNT (2.2 kJ/mm2) was significantly higher than that of the control heat-cured PMMA (1.6 kJ/mm2). Similarly, the Vickers microhardness of the treatment group (52.7 VHN) was significantly higher than that of the control group (19.4 VHN). Regarding the agar diffusion test, after 24 h of incubation, the treated heat-cured PMMA with the Ag-doped CNT exhibited significantly higher anticandidal activity than that of the control group. Therefore, Ag-doped carbon nanotubes could be considered as promising fillers for the dental heat-cured acrylic resin to improve the resistance of the resultant denture against sudden fractures, scratching, and candida invasion.
Keywords: CNT; PMMA; antimicrobial activity; carbon nanotubes; heat-cured acrylic resin; impact strength; poly (methyl methacrylate); silver-doped; surface microhardness.