In this paper, four conductive polyaniline powders doped in hydrochloric acid, sulfuric acid, phosphoric acid, and sulfonic acid were selected and blended with polydimethylsiloxane to prepare coatings with an electromagnetic absorption effect and fouling desorption effect, respectively. A UV spectrophotometer was used to evaluate the settling rate of the powders. Fourier transform infrared spectrometry, laser confocal microscopy, and scanning electron microscopy were used to observe the morphology and structure of the powder and the coating. The interface properties of the coatings were characterized using a contact angle measurement, the mechanical properties of the coatings using a tensile test, and the electromagnetic properties of the powders and microwave absorption properties of the coatings using vector network analyzers. Meanwhile, the antifouling performance of the coatings was evaluated via the marine bacteria adhesion test and benthic diatom adhesion test, and the effect of conductive polyaniline on the antifouling performance of the coating was analyzed. The results show that adding polyaniline reduced the surface energy of the coating and increased the roughness, mechanical properties and anti-fouling properties of the coating. Moreover, adding appropriate polyaniline powder can enhance the electromagnetic wave loss of the coating. The followings values were recorded for a hydrochloric-acid-doped polyaniline coating: lowest surface energy of 17.17 mJ/m2, maximum fracture strength of 0.95 MPa, maximum elongation of 155%, maximum bandwidth of 3.81 GHz, and peak of reflection loss of -23.15 dB. The bacterial detachment rate of the polydimethylsiloxane (PDMS) samples was only 30.37%. The bacterial adhesion rates of the composite coating containing hydrochloric-acid-doped polyaniline were 4.95% and 2.72% after rinsing and washing, respectively, and the desorption rate was 45.35%. The chlorophyll concentration values were 0.0057 mg/L and 0.0028 mg/L, respectively, and the desorption rate was 54.62%.
Keywords: PANI; PDMS; antifouling; coating; electromagnetic performance.