Application of the 316 L stainless steel (SS) is limited by its relatively low wear resistance, insufficient strength, and poor corrosion resistance in special environments. To this end, effects of Mo particles addition on the microstructure, mechanical properties, and corrosion resistance of the laser powder bed fusion (LPBF) 316 L SS are investigated in this study. The results show that the addition of Mo particles from 0 wt.% to 10 wt.% can modify the crystal orientation and improve the strength, wear resistance, and corrosion resistance of LPBF 316 L SSs. Particularly, the LPBF 316 L SS forms a biphasic structure with a similar ratio of α-Fe to γ-Fe with 5 wt.% Mo addition. As a result, the corresponding samples possess both the excellent toughness of austenitic SSs and the high strength and corrosion resistance of ferrite SSs, which reaches a high tensile strength of about 830 MPa, together with a low friction coefficient of 0.421 μ. Since the Mo particles addition is beneficial to increase the content of Cr2O3 on the samples surface from 13.48% to 22.68%, the corrosion current density of 316 L SS decreases by two orders of magnitude from 569 nA to 6 nA, while the mechanical properties remain favorable. This study is expected to serve as a reference for the preparation of LPBF SSs with excellent integrated performance.
Keywords: 316 L stainless steel; corrosion resistance; laser powder bed fusion; mechanical properties.