The outstanding properties of nanofiber composites have made them a popular choice for various structural applications. Recently, there has been a growing interest in using electrospun nanofibers as reinforcement agents, which possess exceptional properties that can enhance the performance of these composites. Herein, TiO2-graphene oxide (GO) nanocomposite incorporated into polyacrylonitrile (PAN)/cellulose acetate (CA) nanofibers were fabricated by an effortless electrospinning technique. The chemical and structural characteristics of the resulting electrospun TiO2-GO nanofibers were examined employing diverse techniques such as XRD, FTIR, XPS, TGA, mechanical properties, and FESEM. Remediation of organic contaminants and organic transformation reactions with electrospun TiO2-GO nanofibers were performed. The results indicated that the incorporation of TiO2-GO with various TiO2/GO ratios did not affect the molecular structure of PAN-CA. Still, they did significantly increase the mean fiber diameter (234-467 nm) and the mechanical properties of the nanofibers comprising UTS, elongation, Young's modulus, and toughness compared to PAN-CA. From various ratios of TiO2/GO (0.01TiO2/0.005GO and 0.005TiO2/0.01GO) in the electrospun NFs, the nanofiber containing a high content of TiO2 showed over 97% of the initial MB dyes were degraded after 120 min of visible light exposure and the same nanofibers also, achieved 96% nitrophenol conversion to aminophenol in just 10 min with activity factor kAF value of 47.7 g-1min-1. These findings illustrate the promise of TiO2-GO/PAN-CA nanofibers for use in various structural applications, particularly in the remediation of organic contaminants from water and organic transformation reactions.
Keywords: Electrospinning; Environmental sustainability; Graphene oxide; Nanofibers; TiO(2); Water remediation.
Copyright © 2023 Elsevier Inc. All rights reserved.