Endowing a single material with various types of luminescence, that is, exhibiting a simultaneous optical response to different stimuli, is vital in various fields. A photoluminescence (PL)- and mechanoluminescence (ML)-based multifunctional sensing platform is built by combining heterojunctioned ZnS/CaZnOS:Mn2+ mechano-photonic materials using a 3D-printing technique and fiber spinning. ML-active particles are embedded in micrometer-sized cellulose fibers for flexible optical devices capable of emitting light driven by mechanical force. Individually modified 3D-printed hard units that exhibit intense ML in response to mechanical deformation, such as impact and friction, are also fabricated. Importantly, they also allow low-pressure sensing up to ≈100 bar, a range previously inaccessible by any other optical sensing technique. Moreover, the developed optical manometer based on the PL of the materials demonstrates a superior high-pressure sensitivity of ≈6.20 nm GPa-1 . Using this sensing platform, four modes of temperature detection can be achieved: excitation-band spectral shifts, emission-band spectral shifts, bandwidth broadening, and lifetime shortening. This work supports the possibility of mass production of ML-active mechanical and optoelectronic parts integrated with scientific and industrial tools and apparatus.
Keywords: lanthanide-doped heterostructures; mechanoluminescence; mechanoluminescent polymers and fibers; pressure and temperature sensors; visual sensors.
© 2023 The Authors. Advanced Materials published by Wiley-VCH GmbH.