The static bending properties, different strain rates and interlaminar shear strength (ILSS) of carbon-fiber-reinforced polymers (CFRP) with two epoxy resins nano-enhanced with carbon nanofibers (CNFs) are studied. The effect on ILSS behavior from aggressive environments, such as hydrochloric acid (HCl), sodium hydroxide (NaOH), water and temperature, are also analyzed. The laminates with Sicomin resin and 0.75 wt.% CNFs and with Ebalta resin with 0.5 wt.% CNFs show significant improvements in terms of bending stress and bending stiffness, up to 10%. The values of ILLS increase for higher values of strain rate, and in both resins, the nano-enhanced laminates with CNFs show better results to strain-rate sensitivity. A linear relationship between the logarithm of the strain rate was determined to predict the bending stress, bending stiffness, bending strain and ILSS for all laminates. The aggressive solutions significantly affect the ILSS, and their effects are strongly dependent on the concentration. Nevertheless, the alkaline solution promotes higher decreases in ILSS and the addition of CNFs is not beneficial. Regardless of the immersion in water or exposure to high temperatures a decrease in ILSS is observed, but, in this case, CNF content reduces the degradation of the laminates.
Keywords: carbon fibers reinforced polymers (CFRP); carbon nanofibers (CNFs); corrosive solutions; interlaminar shear strength; static properties; strain rate.