The present work reports the synthesis of efficient Ti-Au/zeolite Y photocatalysts by different processing of aluminosilicate gel and studies the effect of titania content on the structural, morphological, textural, and optical properties of the materials. The best characteristics of zeolite Y were obtained by aging the synthesis gel in static conditions and mixing the precursors under magnetic stirring. Titania (5, 10, 20%) and gold (1%) species were incorporated in zeolite Y support by the post-synthesis method. The samples were characterized by X-ray diffraction, N2-physisorption, SEM, Raman, UV-Vis and photoluminescence spectroscopy, XPS, H2-TPR, and CO2-TPD. The photocatalyst with the lowest TiO2 loading shows only metallic Au on the outermost surface layer, while a higher content favors the formation of additional species such as: cluster type Au, Au1+, and Au3+. A high TiO2 content contributes to increasing the lifetime of photogenerated charge careers, and the adsorption capacity of the pollutant. Therefore, an increase in the photocatalytic performances (evaluated in degradation of amoxicillin in water under UV and visible light) was evidenced with the titania content. The effect is more significant in visible light due to the surface plasmon resonance (SPR) effect of gold interacting with the supported titania.
Keywords: Ti–Au zeolite Y; aluminosilicate gel; amoxicillin; effect of TiO2 loading; photocatalysis; photodegradation; surface plasmon resonance; zeolite Y.