MOx (M = Zn, Cu, Mn, Fe, Ce) nanoparticles (NPs) embedded in porous C with uniform diameter and dispersion were synthesized, with potential application as S-absorbents to protect catalysts from S-poisoning in catalytic hydrothermal gasification (cHTG) of biomass. S-absorption performance of MOx/C was evaluated by reacting the materials with diethyl disulfide at HTG conditions (450 °C, 30 MPa, 15 min). Their S-absorption capacity followed the order CuOx/C > CeOx/C ≈ ZnO/C > MnOx/C > FeOx/C. S was absorbed in the first four through the formation of Cu1.8S, Ce2S3, ZnS, and MnS, respectively, with a capacity of 0.17, 0.12, 0.11, and 0.09 molS molM-1. The structure of MOx/C (M = Zn, Cu, Mn) evolved significantly during S-absorption reaction, with the formation of larger agglomerates and separation of MOx particles from porous C. The formation of ZnS NPs and their aggregation in place of hexagonal ZnO crystals indicate a dissolution/precipitation mechanism. Note that aggregated ZnS NPs barely sinter under these conditions. Cu(0) showed a preferential sulfidation over Cu2O, the sulfidation of the latter seemingly following the same mechanism as for ZnO. In contrast, FeOx/C and CeOx/C showed remarkable structural stability with their NPs well-dispersed within the C matrix after reaction. MOx dissolution in water (from liquid to supercritical state) was modeled and a correlation between solubility and particle growth was found, comforting the hypothesis of the importance of an Ostwald ripening mechanism. CeOx/C with high structural stability and promising S-absorption capacity was suggested as a promising bulk absorbent for sulfides in cHTG of biomass.
© 2023. The Author(s).