Efficient and zero thermal quenching Sm3+-activated Li2LaTiTaO7 phosphor for white LEDs

Qi Wang; Shangwei Wang; Ran Pang; Taixing Tan; He-Rui Wen; Su Zhang; Hongpeng You; Chengyu Li; Hongjie Zhang

doi:10.1039/d3dt00609c

Efficient and zero thermal quenching Sm³⁺-activated Li₂LaTiTaO₇ phosphor for white LEDs

Dalton Trans. 2023 Jul 4;52(26):9068-9076. doi: 10.1039/d3dt00609c.

Authors

Qi Wang^{1

2

3}, Shangwei Wang^{2

3}, Ran Pang³, Taixing Tan², He-Rui Wen¹, Su Zhang³, Hongpeng You^{1

2

3}, Chengyu Li^{1

2

3}, Hongjie Zhang³

Affiliations

¹ Faculty of Materials Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou, Jiangxi 341000, P. R. China. pangran@ciac.ac.cn.
² Ganjiang Innovation Academy, Chinese Academy of Sciences, Ganzhou 341000, P. R. China.
³ State key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, P. R. China.

PMID: 37337762
DOI: 10.1039/d3dt00609c

Abstract

In this work, we prepared a new orange-red phosphor Li₂La_1-xTiTaO₇:xSm³⁺ (abbreviated as LLTT:Sm³⁺) for white light-emitting diodes (w-LEDs). Its crystal structure, microstructure, photoluminescence characteristics, luminescence lifetime and thermal quenching properties were studied in depth. The LLTT:Sm³⁺ phosphor shows four intense emission peaks at 563, 597, 643, and 706 nm when excited at 407 nm. Thermal quenching is caused by the dipole-quadrupole (d-q) interaction of Sm³⁺ ions, and the optimum doping concentration of Sm³⁺ is x = 0.05. Meanwhile, the LLTT:0.05Sm³⁺ phosphor has a high overall quantum yield (QY = 59.65%) and almost no thermal quenching. The emission intensity at 423 K is 101.5% of the initial value at 298 K, while the CIE chromaticity coordinates barely change as the temperature rises. The fabricated white LED device exhibits excellent CRI and CCT values of 90.4 and 5043 K, respectively. These findings demonstrate that the LLTT:Sm³⁺ phosphor has promise in w-LED applications.