Electrochemical water splitting is an environmentally friendly and effective energy storage method. However, it is still a huge challenge to prepare non-noble metal based electrocatalysts that possess high activity and long-term durability to realize efficient water splitting. Here, we present a novel method of low-temperature phosphating for preparing CoP/Co3 O4 heterojunction nanowires catalyst on titanium mesh (TM) substrate that can be used for oxygen evolution reaction (OER), hydrogen evolution reaction (HER), and overall water splitting. CoP/Co3 O4 @TM heterojunction showed an excellent catalytic performance and long-term durability in 1.0 M KOH electrolyte. The overpotential of CoP/Co3 O4 @TM heterojunction was only 257 mV at 20 mA cm-2 during the OER process, and it could work stably more than 40 h at 1.52 V versus reversible hydrogen electrode (vs. RHE). During the HER process, the overpotential of CoP/Co3 O4 @TM heterojunction was only 98 mV at -10 mA cm-2 . More importantly, when used as anodic and cathodic electrocatalyst, they achieved 10 mA cm-2 at 1.59 V. The Faradaic efficiencies of OER and HER were 98.4 % and 99.4 %, respectively, outperforming Ru/Ir-based noble metal electrocatalysts and other non-noble metal electrocatalysts for overall water splitting.
Keywords: CoP/Co3O4nanowires; electrocatalysis; in-situ heterojunction; overall water splitting.
© 2023 Wiley-VCH GmbH.