We report a high-speed low dark current near-infrared (NIR) organic photodetector (OPD) on a silicon substrate with amorphous indium gallium zinc oxide (a-IGZO) as the electron transport layer (ETL). In-depth understanding of the origin of dark current is obtained using an elaborate set of characterization techniques, including temperature-dependent current-voltage measurements, current-based deep-level transient spectroscopy (Q-DLTS), and transient photovoltage decay measurements. These characterization results are complemented by energy band structures deduced from ultraviolet photoelectron spectroscopy. The presence of trap states and a strong dependency of activation energy on the applied reverse bias voltage point to a dark current mechanism based on trap-assisted field-enhanced thermal emission (Poole-Frenkel emission). We significantly reduce this emission by introducing a thin interfacial layer between the donor: acceptor blend and the a-IGZO ETL and obtain a dark current as low as 125 pA/cm2 at an applied reverse bias of -1 V. Thanks to the use of high-mobility metal-oxide transport layers, a fast photo response time of 639 ns (rise) and 1497 ns (fall) is achieved, which, to the best of our knowledge, is among the fastest reported for NIR OPDs. Finally, we present an imager integrating the NIR OPD on a complementary metal oxide semiconductor read-out circuit, demonstrating the significance of the improved dark current characteristics in capturing high-quality sample images with this technology.
Keywords: Poole−Frenkel emission; Q-DLTS; a-IGZO; activation energy; dark current density; image sensor; near-infrared photodetector; response time.