Effects of size and surface charge on the sedimentation of nanoplastics in freshwater

Abstract

The environmental issues caused by nanoplastics (NPs) are increasingly noticeable. Environmental behavior study of the NPs could provide vital information for their environmental impact assessment. However, associations between NPs' inherent properties and their sedimentation behaviors were seldom investigated. In this study, six types of PSNPs (polystyrene nanoplastics) with different charges (positive and negative) and particle sizes (20-50 nm, 150-190 nm and 220-250 nm) were synthesized, and their sedimentations under different environmental factors, (e.g., pH value, ionic strength (IS), electrolyte type and natural organic matter) were investigated. Results displayed that both particle size and surface charge would affect the sedimentation of PSNPs. The maximum sedimentation ratio of 26.48% was obtained in positive charged PSNPs with size of 20-50 nm, while the minimum sedimentation ratio of 1.02% was obtained in negative charged PSNPs with size of 220-250 nm at pH 7.6. The pH value shift (range of 5-10) triggered negligible changes of sedimentation ratio, the average particle size and the Zeta potential. Small size PSNPs (20-50 nm) showed higher sensitivity to IS, electrolyte type and HA condition than large size PSNPs. At high IS value ( [Formula: see text] = 30 mM or IS_NaCl = 100 mM), the sedimentation ratios of the PSNPs all increased differently according to their properties, and the sedimentation promoting effect of CaCl₂ was more significant on negative charged PSNPs than positive charged PSNPs. When [Formula: see text] increased from 0.9 to 9 mM, the sedimentation ratios of negative charged PSNPs increased by 0.53%-23.49%, while that of positive charged PSNPs increased by less than 10%. Besides, humic acid (HA) addition (1-10 mg/L) would lead to a stable suspension status for PSNPs in water with different degree and perhaps different mechanism due to their charge characteristics. These results showed new light on influence factor studies of NPs' sedimentation and would be helpful for further knowledge of NPs' environmental behaviors.

Keywords: Aggregation; Nanoplastics; Sedimentation; Water environment.