Olefin oligomerization by γ-Al2 O3 has recently been reported, and it was suggested that Lewis acid sites are catalytic. The goal of this study is to determine the number of active sites per gram of alumina to confirm that Lewis acid sites are indeed catalytic. Addition of an inorganic Sr oxide base resulted in a linear decrease in the propylene oligomerization conversion at loadings up to 0.3 wt %; while, there is a >95 % loss in conversion above 1 wt % Sr. Additionally, there was a linear decrease in the intensity of the Lewis acid peaks of absorbed pyridine in the IR spectra with an increase in Sr loading, which correlates with the loss in propylene conversion, suggesting that Lewis acid sites are catalytic. Characterization of the Sr structure by XAS and STEM indicates that single Sr2+ ions are bound to the γ-Al2 O3 surface and poison one catalytic site per Sr ion. The maximum loading needed to poison all catalytic sites, assuming uniform surface coverage, was ∼0.4 wt % Sr, giving an acid site density of ∼0.2 sites per nm2 of γ-Al2 O3 , or approximately 3 % of the alumina surface.
Keywords: Lewis acid sites; acid site poisoning; alumina; propylene oligomerization; strontium single sites.
© 2023 The Authors. ChemPhysChem published by Wiley-VCH GmbH.