Remote epitaxy is a promising technology that has recently attracted considerable attention, which enables the growth of thin films that copy the crystallographic characteristics of the substrate through two-dimensional material interlayers. The grown films can be exfoliated to form freestanding membranes, although it is often challenging to apply this technique if the substrate materials are prone to damage under harsh epitaxy conditions. For example, remote epitaxy of GaN thin films on graphene/GaN templates has not been achieved by a standard metal-organic chemical vapor deposition (MOCVD) method due to such damages. Here, we report GaN remote heteroepitaxy on graphene/AlN templates by MOCVD and investigate the influence of surface pits in AlN on the growth and exfoliation of GaN thin films. We first show the thermal stability of graphene before GaN growth, based on which two-step growth of GaN on graphene/AlN is developed. The GaN samples are successfully exfoliated after the first step of the growth at 750 °C, whereas the exfoliation failed after the second step at 1050 °C. In-depth analysis confirms that the pits in AlN templates lead to the degradation of graphene near the area and thus the alteration of growth modes and the failure of exfoliation. These results exemplify the importance of chemical and topographic properties of growth templates for successful remote epitaxy. It is one of the key factors for III-nitride-based remote epitaxy, and these results are expected to be of great help in realizing complete remote epitaxy using only MOCVD.
Keywords: GaN; exfoliation; graphene; metal−organic chemical vapor deposition; mixed growth; pit; remote heteroepitaxy.