The field of solar vapor generation has developed rapidly in recent years, but achieving the goals of a high evaporation rate, eco-friendliness and rapid preparation with low-cost raw materials is still a challenge. In this work, a type of photothermal hydrogel evaporator was prepared by blending eco-friendly poly(vinyl alcohol), agarose, Fe3+ and tannic acid (TA) together, in which the tannic acid-ferric ion (TA*Fe3+) complexes served as photothermal materials and effective gelators. The results indicate that the TA*Fe3+ complex exhibits excellent gelatinization ability and light-absorption performance, which leads to a compressive stress of 0.98 MPa at 80% strain and up to 85% light absorption ratio in the photothermal hydrogel. For interfacial evaporation, a high rate of 1.897 ± 0.11 kg·m-2·h-1 corresponding to an energy efficiency of 89.7 ± 2.73% under 1 sun irradiation is achieved. Moreover, the hydrogel evaporator exhibits high stability in a 12-hour test and a 20-cycle test without a decline in evaporation performance. The outdoor testing results show that the hydrogel evaporator can achieve an evaporation rate of > 0.70 kg/m2 and effectively purify wastewater treatment and seawater desalination.
Keywords: Hydrogel evaporator; Interfacial solar steam generation; Tannic acid.
Copyright © 2023 Elsevier Inc. All rights reserved.