Oxides are emerging candidates for mid-infrared (mid-IR) nonlinear optical (NLO) materials. However, their intrinsically weak second harmonic generation (SHG) effects hinder their further development. A major design challenge is to increase the nonlinear coefficient while maintaining the broad mid-IR transmission and high laser-induced damage threshold (LIDT) of the oxides. In this study, it is reported on a polar NLO tellurite, Cd2 Nb2 Te4 O15 (CNTO), featuring a pseudo-Aurivillius-type perovskite layered structure composed of three types of NLO active groups, including CdO6 octahedra, NbO6 octahedra, and TeO4 seesaws. The uniform orientation of the distorted units induces a giant SHG response that is ≈31 times larger than that of KH2 PO4 , the largest value among all reported metal tellurites. Additionally, CNTO exhibits a large band gap (3.75 eV), a wide optical transparency window (0.33-14.5 µm), superior birefringence (0.12@ 546 nm), high LIDT (23 × AgGaS2 ), and strong acid and alkali resistance, indicating its potential as a promising mid-IR NLO material.
Keywords: aurivillius-type; grafting-assisted engineering; layered structures; second harmonic generation (SHG) responses.
© 2023 Wiley-VCH GmbH.