Nowadays, industrial adhesives are replacing conventional bonding methods in many industries, including the automotive, aviation, and power industries, among others. The continuous development of joining technology has promoted adhesive bonding as one of the basic methods of joining metal materials. This article presents the influence of surface preparation of magnesium alloys on the strength properties of a single-lap adhesive joint using a one-component epoxy adhesive. The samples were subjected to shear strength tests and metallographic observations. The lowest properties of the adhesive joint were obtained on samples degreased with isopropyl alcohol. The lack of surface treatment before joining led to destruction by adhesive and mixed mechanisms. Higher properties were obtained for samples ground with sandpaper. The depressions created as a result of grinding increased the contact area of the adhesive with the magnesium alloys. The highest properties were noticed for samples after sandblasting. This proved that the development of the surface layer and the formation of larger grooves increased both the shear strength and the resistance of the adhesive bonding to fracture toughness. It was found that the method of surface preparation had a significant influence on the resulting failure mechanism, and the adhesive bonding of the casting of magnesium alloy QE22 can be used successfully.
Keywords: MSR-B/QE22/(MgAg2RE2Zr); adhesive bonding; adhesive layer; magnesium alloy; one-component epoxy; surface treatments.