There is a lack of scientific understanding of adding an oyster shell powder (OSP) to geopolymer concrete. The purpose of this study is: (1) to evaluate the high-temperature resistance of the alkali-activated slag ceramic powder (CP) mixture added with OSP at different temperatures, (2) to address the lack of application of environmentally friendly building materials, and (3) to reduce solid waste of OSP pollution and protect the environment. OSP replaces granulated blast furnace slag (GBFS) and CP at 10% and 20% (based on binder), respectively. The mixture was heated to 400.0, 600.0, and 800.0 °C after curing for 180 days. The results of the experiment are summarized as follows: (1) The thermogravimetric (TG) results indicated that the OSP20 samples produced more CASH gels than the control OSP0. (2) As the temperature increased, the compressive strength and ultrasonic pulse velocity (UPV) both decreased. (3) Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) results reveal that the mixture undergoes a phase transition at 800.0 °C, and compared with the control OSP0, OSP20 undergoes a different phase transition. (4) The size change and appearance image results indicate that the mixture with added OSP inhibits shrinkage, and calcium carbonate decomposes to produce off-white CaO. To sum up, adding OSP can effectively reduce the damage of high temperatures (800.0 °C) on the properties of alkali-activated binders.
Keywords: alkaline activator; microscopic analysis; phase transition; size changes.