The effect of the stereoregularity of poly(1-trimethylsilyl-1-propyne) [PTMSP] (cis-content from 50 to 90%) on physical aging was investigated by measurement of the gas permeability. Films from pure PTMSP as well as those with the addition of the antioxidant Irganox 1076 were exposed to the air. The permeability of pure PTMSP films increases with an increase in cis-stereoregularity and correlates with an increase in interchain distances (according to X-ray analysis). For pure PTMSP films, the most significant aging (up to 50% of permeability drop) was observed for polymers with mixed microstructure, and the slowest aging (10-30% of permeability drop) was observed for polymers with cis-regular structure. For PTMSP films with added Irganox 1076, some decrease in permeability with time is also observed. The addition of Irganox 1076 to PTMSP in mixed as well as cis-enriched configurations visibly slows down aging. In the case of cis-regular PTMSP with a slow aging rate, the introduction of an antioxidant does not provide any advantages. The high stability of cis-regular PTMSP demonstrates the possibility of obtaining more stable membrane materials with the highest equilibrium state of the polymer selective layer prepared by casting solution.
Keywords: aging; gas permeation; high free volume polymer; membranes; poly(1-trimethylsilyl-1-propyne).