The dissolution of carbides during the heating to the quenching temperature has a significant effect on the martensite oversaturation and the resulting mechanical properties. The kinetics of dissolution can be influenced by various external factors. This work deals with monitoring the carbide dissolution utilizing dilatometer analysis. The austenitization of 100CrMnSi6-4 bearing steel in two initial states was compared-after accelerated spheroidization annealing and conventional soft annealing. The main objective was to determine the amount of undissolved cementite during austenitization in the temperature range where only austenite and cementite are present in the structure. The austenitization temperature determines the degree of cementite dissolution and, consequently, the carbon content in austenite and thus the final properties after quenching. The cementite dissolution was quantified from dilatometric curves and image analysis.
Keywords: 100CrMnSi6-4 bearing steel; austenitization; carbide; dissolution; induction; spheroidization; transformation temperature.