A comprehensive comparison of electrochemical capacitors (ECs) with various aqueous alkali metal sulfate solutions (Li2SO4, Na2SO4, Rb2SO4, and Cs2SO4) is reported. The EC with a less conductive 1 mol L-1 Li2SO4 solution demonstrates the best long-term performance (214 h floating test) compared to the EC with a highly conductive 1 mol L-1 Cs2SO4 solution (200 h). Both the positive and negative EC electrodes are affected by extensive oxidation and hydrogen electrosorption, respectively, during the aging process, as proven by the SBET fade. Interestingly, carbonate formation is observed as a minor cause of aging. Two strategies for optimizing sulfate-based ECs are proposed. In the first approach, Li2SO4 solutions with the pH adjusted to 3, 7, and 11 are investigated. The sulfate solution alkalization inhibits subsequent redox reactions, and as a result, EC performance is successfully enhanced. The second approach exploits so-called bication electrolytic solutions based on a mixture of Li2SO4 and Na2SO4 at an equal concentration. This concept allows the operational time to be significantly prolonged, up to 648 h (+200% compared to 1 mol L-1 Li2SO4). Therefore, two successful pathways for improving sulfate-based ECs are demonstrated.
Keywords: activated carbon electrode; aging; aqueous electrolyte; electrochemical capacitor; prolonged lifetime; sulfate-based capacitors.